| NYLON 6/6 33% GLASSFILLED HEAT STABILIZED NEW TEXT | ||||
| TICONA CELANESE® 33% GLASS-FIBER REINFORCED HEAT STABILIZED NYLON TYPE 6/6-1503-2P | ||||
| Ticona Celanese® / Nylon Type 6/6-1503-2P | ||||
| Glass-Reinforced
nylon heat stabilized has the same mechanical properties as
glass-reinforced nylon with the additional advantage of heat stabilization. This material can withstand 250 °F (121 °C) temperatures in long range service in most applications. Glass-Reinforced heat stabilized nylon is medium brown in color. |
||||
| APPLICATIONS | ||||
| Fasteners
– Washers – Spacers – Insulators – Circuit Board Hardware –
Requiring greater stiffness and strength. |
||||
| Approvals | Underwriters Laboratory UL File E39806 | |||
| Federal Specification Type 1 Class 2 L-P-395B | ||||
| Properties | ||||
| Physical | Units | Test Method | DAM | 50% RH |
| Specific Gravity | ASTM D792 | 1.38 | * | |
| Density | lbs/in3 | ASTM D792 | 0.0498 | * |
| Water Absorption (24 hours @ 73°F) | % | ASTM D570 | 1.0 | * |
| Mechanical | Units | Test Method | DAM | 50% RH |
| Tensile Strength | psi | ASTM D638 | 28,000 | 22,000 |
| Elongation at Break | % | ASTM D638 | 2-4 | 3-5 |
| Shear Strength | psi | ASTM D732 | 13,000 | 10,000 |
| Compressive Strength | psi | ASTM D695 | 28,000 | 22,000 |
| Flexural Strength | psi | ASTM D790 | 40,000 | 29,000 |
| Flexural Modulus | psi | ASTM D790 | 1.2x106 | 0.9x106 |
| Impact | Units | Test Method | DAM | 50% RH |
| Izod Impact (Notched) | ft-lb/in | ASTM D256 | 2.2 | 2.6 |
| Tensile Impact | ft-lb/in2 | ASTM D1822 | 70 | 80 |
| Thermal | Units | Test Method | DAM | 50% RH |
| Melting Point | °F | ASTM D789 | 495 | 495 |
| Deflection Temperature (.46 Mpa) | ||||
| 66 psi | °F | ASTM D648 | 495 | * |
| 264 psi | °F | ASTM D648 | 485 | * |
| Specific Heat (1.82 Mpa) | 0.3 | * | ||
| Thermal Conductivity | BTU/m/ft2°F/in | 1.5 | * | |
| Coefficient of Linear Thermal Expansion | in/in/°F | ASTM D696 | 1.6x105 | * |
| Elevated Temperature Service | ||||
| Long Range Service | °F | 250 | * | |
| Long Range Service in Water | °F | 125 | * | |
| Intermittent Exposure | °F | 300 | * | |
| Elcetrical | Units | Test Method | DAM | 50% RH |
| Dielectric Strength | v/mil | ASTM D149 | 400 | * |
| Dielectric Constant | ||||
| @ 60 Hertz | ASTM D150 | 4.1 | * | |
| @ 100 Hertz | ASTM D150 | * | * | |
| @ 1000 Hertz | ASTM D150 | 4.0 | * | |
| Volume Resistivity | ohm-om | ASTM D257 | 1014 | * |
| Power Factor | ||||
| @ 60 Hertz | ASTM D150 | 0.006 | * | |
| @ 100 Hertz | ASTM D150 | * | * | |
| @ 1000 Hertz | ASTM D150 | 0.009 | * | |
| Hardness | Units | Test Method | DAM | 50% RH |
| Hardness | Rockwell | ASTM D785 | M100 | M82 |
| Miscellaneous | Units | Test Method | DAM | 50% RH |
| Taber Abrasion (CS-17 wheel 1000 gram load) | mg/1000 cycles | ASTM D1044 | 20 | 16 |
| Coefficient of Friction | ASTM D1894 | |||
| Dynamic | ||||
| vs. itself | 0.23 | * | ||
| vs. steel | 0.15 | 0.17 | ||
| vs. aluminum | 0.12 | 0.13 | ||
| vs. brass | 0.11 | 1.24 | ||
| Flammability | in/min | ASTM D635 | 1.1 | * |
| UL94 | HB | |||